Zirconia-related phases in the zirconia/titanium diffusion couple after annealing at 1100°-1550°C

Kun Lin Lin, Chien-Cheng Lin*

*此作品的通信作者

研究成果: Article同行評審

20 引文 斯高帕斯(Scopus)

摘要

A diffusion couple of 3 mol% Y2O3-ZrO2 and titanium was isothermally annealed in argon at temperatures between 1100° and 1550°C. The phases and microstructure in the ceramic side were investigated using scanning electron microscopy and transmission electron microscopy, both attached to an energy-dispersive spectrometer. After annealing at 1100°C/6 h, zirconia grains did not grow conspicuously and evolved only traces of oxygen, resulting in t-ZrO2-x but α-Zr. At temperatures above 1300°C, a significant amount of oxygen evolved from zirconia, reducing the O/Zr ratio, such that α-Zr was excluded from t-ZrO2-x during cooling, yielding a higher O/Zr ratio (≈ 2). When held at 1550°C/6 h, zirconia grains grew rapidly. The α-Zr was segregated on grain boundaries during cooling by the exsolution of zirconium from ZrO2-x, while twinned t′-ZrO2-x or lenticular t-ZrO2-x, which was embedded in ordered c-ZrO2-x, was found. The ordered c-ZrO2-x was identified by the 1/5 {113} superlattice reflections of its electron diffraction patterns.

原文English
頁(從 - 到)2928-2934
頁數7
期刊Journal of the American Ceramic Society
88
發行號10
DOIs
出版狀態Published - 十月 2005

指紋

深入研究「Zirconia-related phases in the zirconia/titanium diffusion couple after annealing at 1100°-1550°C」主題。共同形成了獨特的指紋。

引用此