X-ray and dielectric studies of hot-pressed K2Sr4Nb10O30 ceramics

O. A. Bunina, Yu A. Kuprina, I. P. Raevski*, Ya S. Knyazeva, S. I. Raevskaya, Haydn Chen, C. C. Chou, V. V. Titov, D. Mezzane, E. I. Sitalo

*此作品的通信作者

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

X-ray diffraction (XRD) and dielectric studies of dense hot-pressed K2Sr4Nb10O30 ceramics with a tetragonal tungsten bronze–type structure revealed texturing of the samples and substantial anisotropy of the dielectric permittivity. XRD studies of the K2Sr4Nb10O30 powder show a diffuse phase transition in the 140 – 160°C range while a diffused and frequency-independent maximum of the dielectric permittivity is observed at about 120–125°C for ceramic samples. Substantial anisotropy of the dielectric permittivity (more than 50% in the phase transition region) as well as sample's texturing and a difference between phase transition temperatures of the powder and ceramic samples are supposed to be caused by anisotropic residual stresses.

原文English
頁(從 - 到)145-153
頁數9
期刊Ferroelectrics
501
發行號1
DOIs
出版狀態Published - 1 九月 2016

指紋

深入研究「X-ray and dielectric studies of hot-pressed K<sub>2</sub>Sr<sub>4</sub>Nb<sub>10</sub>O<sub>30</sub> ceramics」主題。共同形成了獨特的指紋。

引用此