Tuning the magnetic resonance imaging properties of positive contrast agent nanoparticles by surface modification with RAFT polymers

Misty D. Rowe, Chia Chih Chang, Douglas H. Thamm, Susan L. Kraft, Joseph F. Harmon, Andrew P. Vogt, Brent S. Sumerlin, Stephen G. Boyes

研究成果: Article同行評審

112 引文 斯高帕斯(Scopus)

摘要

A novel surface modification technique was employed to produce a polymer modified positive contrast agent nanoparticle through attachment of well-defined homopolymers synthesized via reversible addition-fragmentation chain transfer (RAFT) polymerization. A range of RAFT homopolymers including poly[N-(2-hydroxypropyl) methacrylamide], poly(N-isopropylacrylamide), polystyrene, poly(2-(dimethylamino)ethyl acrylate), poly(((poly)ethylene glycol) methyl ether acrylate), and poly(acrylic acid) were synthesized and subsequently used to modify the surface of gadolinium (Gd) metal-organic framework (MOF) nanoparticles. Employment of a trithiocarbonate RAFT agent allowed for reduction of the polymer end groups under basic conditions to thiolates, providing a means of homopolymer attachment through vacant orbitais on the Gd3+ ions at the surface of the Gd MOF nanoparticles. Magnetic resonance imaging (MRI) confirmed the relaxivity rates of these novel polymer modified structures were easily tuned by changes in the molecular weight and chemical structures of the polymers. When a hydrophilic polymer was used for modification of the Gd MOF nanoparticles, an increase in molecular weight of the polymer provided a respective increase in the longitudinal relaxivity. These relaxivity values were significantly higher than both the unmodified Gd MOF nanoparticles and the clinically employed contrast agents, Magnevist and Multihance, which confirmed the construct's ability to be utilized as a positive contrast nanoparticle agent in MRI. Further characterization confirmed that increased hydrophobicity of the polymer coating on the Gd MOF nanoparticles yielded minimal changes in the longitudinal relaxivity properties but large increases in the transverse relaxivity properties in the MRI.

原文English
頁(從 - 到)9487-9499
頁數13
期刊Langmuir
25
發行號16
DOIs
出版狀態Published - 18 8月 2009