Three-orthogonal-direction stress mapping around a fatigue-crack tip using neutron diffraction

E-Wen Huang*, Soo Yeol Lee, Wanchuck Woo, Kuan Wei Lee

*此作品的通信作者

研究成果: Article同行評審

7 引文 斯高帕斯(Scopus)

摘要

Instrument Scientist, is with the Neutron Science Division, Korea Atomic Energy Research Institute, Daejeon 305-353, South Korea Quantitative determination of the stress fields around the crack tip is a challenging and important subject to understand the fatigue crack-growth mechanism. In the current study, we measured the distribution of residual stresses and the evolution of the stress fields around a fatigue crack tip subjected to the constant-amplitude cyclic loading in a 304L stainless steel compact-tension (CT) specimen. The three orthogonal stress components (i.e., crack growth, crack opening, and through thickness) of the CT specimen were determined as a function of distance from the crack tip with 1-mm spatial resolution along the crack-propagation direction. In-situ neutron-diffraction results show that the enlarged tensile stresses were developed during loading along the through-thickness direction at a localized volume close to the crack tip, resulting in the lattice expansion in all three orthogonal directions during Pmax. The current study suggests that the atypical plane strainlike behavior observed at the midthickness position might be the reason for the mechanism of the faster crack-growth rate inside the interior than that near the surface.

原文English
頁(從 - 到)2785-2791
頁數7
期刊Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
43
發行號8
DOIs
出版狀態Published - 1 八月 2012

指紋

深入研究「Three-orthogonal-direction stress mapping around a fatigue-crack tip using neutron diffraction」主題。共同形成了獨特的指紋。