Synthesis of neutral SiO2/TiO2 hydrosol and its photocatalytic degradation of nitric oxide gas

Chia Hung Huang*, Hsun-Ling Bai, Shu Ling Liu, Yao Ling Huang, Yao Hsuan Tseng

*此作品的通信作者

研究成果: Article同行評審

21 引文 斯高帕斯(Scopus)

摘要

A neutral transparent SiO2/TiO2 composite hydrosol was prepared by a coprecipitation-peptisation method using titanium tetrachloride and SiO2 hydrosol as raw materials. The prepared SiO2/TiO2 hydrosols were characterised by X-ray diffraction, Fourier transform infrared spectroscopy and transmission electron microscopy. The evaluation of photocatalytic activity for nitric oxide degradation showed the optimal weight ratio of SiO2/TiO2 is around 1.5. After heating at 700°C for 1h, the prepared SiO 2/TiO2 hydrosol exhibits much higher photocatalytic activity than the commercial TiO2 materials, Degussa P25 and ONID TH. The presence of Ti-O-Si bond in the composite hydrosol results in its good thermal stability. The prepared transparent SiO2/TiO2 hydrosols were stable without agglomeration or gelation after storage at room temperature for over 1.5 years. The neutral SiO2/TiO2 hydrosol could be used as the coating material applying for glass or ceramic building materials which must be treated at high temperature.

原文English
頁(從 - 到)646-649
頁數4
期刊Micro and Nano Letters
6
發行號8
DOIs
出版狀態Published - 1 8月 2011

指紋

深入研究「Synthesis of neutral SiO2/TiO2 hydrosol and its photocatalytic degradation of nitric oxide gas」主題。共同形成了獨特的指紋。

引用此