Synthesis of La0.6Ca0.4Co0.8Ir0.2O3 perovskite for bi-functional catalysis in an alkaline electrolyte

Yun Min Chang, Pu-Wei Wu*, Cheng Yeou Wu, Yu Chi Hsieh

*此作品的通信作者

研究成果: Article同行評審

34 引文 斯高帕斯(Scopus)

摘要

The amorphous citrate precursor method was employed to prepare perovskite of La0.6Ca0.4Co0.8Ir0.2O3 as a bi-functional electrocatalyst for oxygen reduction and evolution in an alkaline electrolyte. The X-ray diffraction pattern of the as-synthesized powders exhibited a majority phase identical to that of La0.6Ca0.4CoO3, indicating successful incorporation of Ir4+ at the Co cation sites. Scanning Electron Microscope images demonstrated a foam-like microstructure with a surface area of 13.31 m2 g-1. For electrochemical characterization, the La0.6Ca0.4Co0.8Ir0.2O3 particles were supported on carbon nanocapsules (CNCs) and deposited on commercially available gas diffusion electrodes with a loading of 2.4 mg cm-2. In current-potential polarizations, La0.6Ca0.4Co0.8Ir0.2O3/CNCs revealed more enhanced bi-functional catalytic abilities than La0.6Ca0.4CoO3/CNCs. Similar behaviors were observed in galvanostatic profiles for oxygen reduction and evolution at current densities of 50 and 100 mA cm-2 for 10 min. Moreover, notable changes from zeta potential measurements were recorded for La0.6Ca0.4Co0.8Ir0.2O3 relative to La0.6Ca0.4CoO3. In lifetime determinations, where a repeated 3 h sequence of oxygen reduction/resting/oxygen evolution/resting was imposed, La0.6Ca0.4Co0.8Ir0.2O3/CNCs delivered a stable and sustainable behavior with moderate degradation.

原文English
頁(從 - 到)1003-1007
頁數5
期刊Journal of Power Sources
189
發行號2
DOIs
出版狀態Published - 15 四月 2009

指紋

深入研究「Synthesis of La0.6Ca0.4Co0.8Ir0.2O3 perovskite for bi-functional catalysis in an alkaline electrolyte」主題。共同形成了獨特的指紋。

引用此