Synthesis and optical properties of ZnO-ZnS core-shell nanotube arrays

Hung Chou Liao, Pai Chia Kuo, Chin Ching Lin, San-Yuan Chen*

*此作品的通信作者

研究成果: Article同行評審

36 引文 斯高帕斯(Scopus)

摘要

Heterostructured ZnO-ZnS core-shell nanotube arrays with the diameters of 50-80 nm and lengths up to 1 μm were synthesized by a two-step chemical reaction. First, the ZnO layer was grown by atomic-layer deposition. It was found that the preferred growth orientation was strongly dependent on the substrate temperature. After sulfuration conversion from arrayed ZnO nanorods, the ZnS-ZnO composite arrays can be successfully prepared, as evidenced from transmission electron microscopy. This confirms that the ZnO-ZnS core-shell nanotube-arrayed structure has been fabricated. X-ray photoelectron spectroscopy analysis indicates that the binding energy of S 2p is the same as that of bulk single-crystal ZnS and that the Zn 2p3/2 peak is shifted about 0.5 eV due to the formation of Zn-S bonds. Photoluminescence shows the relative-intensity ratio of ultraviolet emission (IUV) to deep-level emission (IDLE) for ZnO/ZnS core-shell nanotubes can be enhanced to be nine times that of original ZnO nanotubes.

原文English
頁(從 - 到)2198-2201
頁數4
期刊Journal of Vacuum Science and Technology B: Microelectronics and Nanometer Structures
24
發行號5
DOIs
出版狀態Published - 9 10月 2006

指紋

深入研究「Synthesis and optical properties of ZnO-ZnS core-shell nanotube arrays」主題。共同形成了獨特的指紋。

引用此