Study of Al interdiffusion in ultrathin β-Ta/Co2FeAl/MgO heterostructures for enhanced spin-orbit torque

Vishal Bhardwaj, Kuan Ming Chen, Yuan Chieh Tseng, Ratnamala Chatterjee*

*此作品的通信作者

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

In this work perpendicular magnetization of Co2FeAl (CFA) full-Heusler alloy films is achieved using rapid thermal annealing under N2/H2 gas flow in Si/β-Ta(6.5 nm)/CFA(0.6–2 nm)/MgO(1.15 nm)/Pd(1 nm) heterostructures. The Al interdiffusion into MgO layer plays an important role in determining perpendicular magnetic anisotropy(PMA) and increasing the damping constant (α) of ultrathin CFA samples. The time of flight SIMS depth profiling along with XPS is used to study interdiffusion of Al across CFA/MgO interface. XPS analysis of Al-2p and Mg-1s spectra indicate the formation of Al2O3 and MgAl2Ox oxide phases at CFA/MgO interface in addition to pure Al metal. The Slonczewski-like and the field-like SOT effective fields are quantified using second harmonics measurements. An effective spin hall angle of β-Ta (6.5 nm) is estimated in range −0.02 to −0.06 for CFA layer thickness varied from 0.8 nm to 1.5 nm.

原文English
文章編號411662
期刊Physica B: Condensed Matter
574
DOIs
出版狀態Published - 1 十二月 2019

指紋

深入研究「Study of Al interdiffusion in ultrathin β-Ta/Co<sub>2</sub>FeAl/MgO heterostructures for enhanced spin-orbit torque」主題。共同形成了獨特的指紋。

引用此