Structural variations in the ternary system HfAl2-xCu x (x = 0.2-1.0)

Wen Heng Huang, Chi-Shen Lee*

*此作品的通信作者

    研究成果: Article同行評審

    摘要

    Synthesized ternary intermetallic phases HfAl2-xCux in a series with (x = 0.49, 0.88, 1.04) are characterized as Laves phase structures. X-ray diffraction revealed homogeneity within ranges 0.2 ≤ x ≤ 0.5 and 0.7 ≤ x ≤ 0.9 for structure types MgCu2 and MgNi 2, respectively. When Cu atoms gradually replaced the Al atoms, the structure type altered in the sequence MgCu2 → MgNi2 → MgZn2, and the Kagomé nets were distorted with varied bond lengths. Measurements of physical properties revealed these phases to be metallic, with resistances 4.35 (x = 0.5), 5.85 (x = 0.7), and 6.50 (x = 0.9) mΩ cm, respectively, at temperature 300 K. The coloring schemes reveal that, upon increasing the proportion of Cu atoms, the stability of these phases correlated with the arrangements of the Al and Cu atoms. Calculated electronic structures indicate that the bonding character is consistent with the experimentally observed phase width.

    原文English
    頁(從 - 到)1849-1856
    頁數8
    期刊Intermetallics
    19
    發行號12
    DOIs
    出版狀態Published - 1 十二月 2011

    指紋

    深入研究「Structural variations in the ternary system HfAl<sub>2-x</sub>Cu <sub>x</sub> (x = 0.2-1.0)」主題。共同形成了獨特的指紋。

    引用此