Structural evolution and copper-ion release behavior of Cu-pHEMA hybrids synthesized in situ

Yen Yu Liu, Tsan Hua Tung, Kun Ho Liu, San-Yuan Chen, Dean-Mo LIu*

*此作品的通信作者

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)

摘要

A novel Cu-pHEMA hybrid was successfully prepared by in situ photopolymerization of 2-hydroxyethyl methacrylate (HEMA) monomer in the presence of Cu(II) copper ions, following an in situ chemical reduction. Experimental observations indicate that intermolecular interactions such as the coupling force and hydrogen bonding between the Cu and the hydroxyl groups further stabilize the hybrid structure to a considerable extent. Localization of the metallic copper particles within the pHEMA network structure as a result of those intermolecular interactions gives rise to the formation of discretely distributed nanocrystallites with particle sizes ranging from 5 to 25 nm in diameter. A crystallographic change of the Cu nanophase from an amorphous-like to a crystalline structure is observed as the H2O:HEMA molar ratio increases, upon synthesis, accompanied with an increase in the particle size. A relatively slow and sustained release of the Cu (in the form of cupric ions) from the hybrids was measured for a time period of about 10 days, which also illustrates a Cu(II)-induced proliferation of the endothelial cells over a relatively small range of release rate of the Cu from the hybrids. Such a new type of Cu-loaded hybrid hydrogel is expected to be compatible and may be considered as a candidate biomaterial for biomedical/therapeutic uses.

原文English
期刊Advanced Engineering Materials
11
發行號11
DOIs
出版狀態Published - 1 十一月 2009

指紋

深入研究「Structural evolution and copper-ion release behavior of Cu-pHEMA hybrids synthesized in situ」主題。共同形成了獨特的指紋。

引用此