Structural and electrical characteristics of low-dielectric constant porous hydrogen silsesquioxane for Cu metallization

J. H. Wang, W. J. Chen, T. C. Chang, Po-Tsun Liu, S. L. Cheng, J. Y. Lin, L. J. Chen*

*此作品的通信作者

研究成果: Article同行評審

15 引文 斯高帕斯(Scopus)

摘要

The structural and electrical properties of porous hydrogen silsesquioxane (XLK) have been characterized using a combination of Fourier transform infrared spectroscopy, transmission electron microscope, Auger electron spectroscopy, current-voltage analyzer, and capacitance-voltage analyzer. The pores, about 2 nm in size and of spherical shape, were distributed randomly and uniformly in the XLK film. The dielectric constant of XLK film was as low as 2.1 owing to the high porosity and uniformity of the film. A smooth amorphous-like layer including Cu-O-Si was found to form between Cu and the XLK film after annealing at 500°C for 30 min. The mixed layer led to the higher leakage current of the XLK film. Cu was found to diffuse into XLK film after annealing at 600°C for 30 min.

原文English
頁(從 - 到)F141-F146
頁數6
期刊Journal of the Electrochemical Society
150
發行號8
DOIs
出版狀態Published - 8月 2003

指紋

深入研究「Structural and electrical characteristics of low-dielectric constant porous hydrogen silsesquioxane for Cu metallization」主題。共同形成了獨特的指紋。

引用此