Spectroscopic signatures for interlayer coupling in MoS2-WSe2 van der waals stacking

Ming Hui Chiu, Ming Yang Li, Wengjing Zhang, Wei Ting Hsu, Wen-Hao Chang, Mauricio Terrones, Humberto Terrones, Lain Jong Li*

*此作品的通信作者

研究成果: Article同行評審

205 引文 斯高帕斯(Scopus)

摘要

Stacking of MoS2 and WSe2 monolayers is conducted by transferring triangular MoS2 monolayers on top of WSe2 monolayers, all grown by chemical vapor deposition (CVD). Raman spectroscopy and photoluminescence (PL) studies reveal that these mechanically stacked monolayers are not closely coupled, but after a thermal treatment at 300 °C, it is possible to produce van der Waals solids consisting of two interacting transition metal dichalcogenide (TMD) monolayers. The layer-number sensitive Raman out-of-plane mode A2 1g for WSe2 (309 cm-1) is found sensitive to the coupling between two TMD monolayers. The presence of interlayer excitonic emissions and the changes in other intrinsic Raman modes such as E′ for MoS2 at 286 cm-1 and A2 1g for MoS2 at around 463 cm-1 confirm the enhancement of the interlayer coupling.

原文English
頁(從 - 到)9649-9656
頁數8
期刊ACS Nano
8
發行號9
DOIs
出版狀態Published - 23 九月 2014

指紋

深入研究「Spectroscopic signatures for interlayer coupling in MoS<sub>2</sub>-WSe<sub>2</sub> van der waals stacking」主題。共同形成了獨特的指紋。

引用此