Properties and reliability of Ta2O5 thin films deposited on Ta

S. Ezhilvalavan*, Tseung-Yuen Tseng


    研究成果: Conference article同行評審

    3 引文 斯高帕斯(Scopus)


    The electrical and reliability properties of reactively sputtered Ta2O5 thin films with Ta as the bottom electrodes forming simple metal insulator metal (MIM) structure. Pt/Ta2O5/Ta/SiO2/n-Si were studied. Ta films were deposited on SiO2/n-Si substrates by sputtering in Ar and in situ annealed at 700°C for 10 min in N2 at a chamber pressure of 20 mTorr. We compared the effectiveness of both as-deposited and annealed Ta bottom electrode on the leakage characteristics of Ta2O5 thin films. Ta2O5 films subjected to rapid thermal annealing (RTA) process at 800°C for 30s in O2 crystallized the film, decreased the leakage current density and resulted in reliable time-dependent dielectric breakdown characteristics. We also envisaged the influence of the surface roughness and morphology of the Ta bottom electrode in modifying the resultant microstructure of the annealed Ta2O5 films. Present studies demonstrate the use of Ta as a potential bottom electrode material replaces the precious metal electrodes and simplifies the fabrication process of the Ta2O5 storage capacitor.

    頁(從 - 到)1042-1046
    期刊Proceedings - Electronic Components and Technology Conference
    出版狀態Published - 1 1月 1999
    事件Proceedings of the 1999 49th Electronic Components and Technology Conference (ECTC) - San Diego, CA, USA
    持續時間: 1 6月 19994 6月 1999


    深入研究「Properties and reliability of Ta2O5 thin films deposited on Ta」主題。共同形成了獨特的指紋。