Photovoltaic and flexible deep ultraviolet wavelength detector based on novel β-Ga2O3/muscovite heteroepitaxy

Bhera Ram Tak*, Ming Min Yang, Yu Hong Lai, Ying-hao Chu, Marin Alexe, Rajendra Singh

*此作品的通信作者

研究成果: Article同行評審

2 引文 斯高帕斯(Scopus)

摘要

Flexible and self-powered deep ultraviolet (UV) photodetectors are pivotal for next-generation electronic skins to enrich human life quality. The fabrication of epitaxial β-Ga2O3 thin films is challenging on flexible substrates due to high-temperature growth requirements. Herein, β-Ga2O3 (2 - 0 1) films are hetero-epitaxially grown on ultra-thin and environment-friendly muscovite mica which is the first time β-Ga2O3 epitaxy growth on any flexible substrate. Integration of Gallium oxide with muscovite enables high-temperature processing as well as excellent flexibility compared to polymer substrates. Additionally, the metal–semiconductor-metal (MSM) photodetector on β-Ga2O3 layer shows an ultra-low dark current of 800 fA at zero bias. The photovoltaic peak responsivity of 11.6 µA/W is obtained corresponding to very weak illumination of 75 μW/cm2 of 265 nm wavelength. Thermally stimulated current (TSC) measurements are employed to investigate the optically active trap states. Among these traps, trap with an activation energy of 166 meV dominates the persistence photocurrent in the devices. Finally, photovoltaic detectors have shown excellent photocurrent stability under bending induced stress up to 0.32%. Hence, this novel heteroepitaxy opens the new way for flexible deep UV photodetectors.

原文English
文章編號16098
期刊Scientific reports
10
發行號1
DOIs
出版狀態Published - 1 十二月 2020

指紋

深入研究「Photovoltaic and flexible deep ultraviolet wavelength detector based on novel β-Ga<sub>2</sub>O<sub>3</sub>/muscovite heteroepitaxy」主題。共同形成了獨特的指紋。

引用此