Performance comparison of III–V//Si and III–V//InGaAs multi-junction solar cells fabricated by the combination of mechanical stacking and wire bonding

The integration of III–V and Si multi-junction solar cells as photovoltaic devices has been studied in order to achieve high photovoltaic conversion efficiency. However, large differences in the coefficients of thermal expansion and the lattice parameters of GaAs, Si, and InGaAs have made it difficult to obtain high-efficiency solar cells grown as epilayers on Si and InP substrates. In this paper, two types of devices, including GaInP/GaAs stacked on Si (GaInP/GaAs//Si) and GaInP/GaAs stacked on InGaAs (GaInP/GaAs//InGaAs), are fabricated via mechanical stacking and wire bonding technologies. Mechanically stacked GaInP/GaAs//Si and GaInP/GaAs//InGaAs triple-junction solar cells are prepared via glue bonding. Current-voltage measurements of the two samples are made at room temperature. The short-circuit current densities of the GaInP/GaAs//Si and GaInP/GaAs//InGaAs solar cells are 13.37 and 13.66 mA/cm ² , while the open-circuit voltages of these two samples are measured to be 2.71 and 2.52 V, respectively. After bonding the GaInP/GaAs dual-junction with the Si and InGaAs solar cells, the conversion efficiency is relatively improved by 32.6% and 30.9%, respectively, compared to the efficiency of the GaInP/GaAs dual-junction solar cell alone. This study demonstrates the high potential of combining mechanical stacked with wire bonding and ITO films to achieve high conversion efficiency in solar cells with three or more junctions.