Novel yellowish-orange Sr8Al12O24S2:Eu2+ phosphor for application in blue light-emitting diode based white LED

Te Wen Kuo, Chien Hao Huang, Teng-Ming Chen

研究成果: Article同行評審

41 引文 斯高帕斯(Scopus)

摘要

A new yellowish-orange phosphor, Sr8Al12O24S2:Eu2+, was synthesized by the solid-state method and its photoluminescence properties were investigated by excitation and emission spectra. Its excitation band is extending from 400-500 nm, which is adaptable to the emission band of blue LED chips (450-470 nm). Upon the excitation of 450 nm light, the phosphor exhibits strong yellowish-orange emission centered at 605 nm with good thermal stability. A white light-emitting diode (W-LED) that consists of a blue LED chip (70 nm) and a (Sr0.92Eu0.08)8Al12O24S2 phosphor is demonstrated. The CIE1931 chromaticity coordinates (x, y) are (0.34, 0.25), the correlated color temperature (CCT) is 4300 K, and the luminous efficacy of this W-LED is 14.2 lm/W at room temperature and with a forward-bias current of 400 mA.

原文English
頁(從 - 到)A231-A236
期刊Optics Express
18
發行號102
DOIs
出版狀態Published - 21 六月 2010

指紋

深入研究「Novel yellowish-orange Sr<sub>8</sub>Al<sub>12</sub>O<sub>24</sub>S<sub>2</sub>:Eu<sup>2+</sup> phosphor for application in blue light-emitting diode based white LED」主題。共同形成了獨特的指紋。

引用此