Microwave properties of a Y0.7Ca0.3Ba 2Cu3O7-δ microstrip ring resonator with various hole concentrations

L. S. Lai*, Jenh-Yih Juang, Kaung-Hsiung Wu, T. M. Uen, Jiunn-Yuan Lin, Y. S. Gou

*此作品的通信作者

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

Superconducting ring resonator with a Y0.7Ca 0.3Ba2Cu3O7-δ ground plane was fabricated by using Y0.7Ca0.3Ba2Cu 3O7-δ thin film deposited on both sides of a LaAlO3 (LAO) substrate. The resonator exhibits a high quality factor Q > 104 at T < 30 K, and from empirical relation, T c/Tc,max = 1 - 82.6(p - 0.16)2, we obtained the hole concentration p. By controlling the oxygen contents of the ring resonator, the hole concentration p was controlled from 0.218 to 0.088, determined by the empirical relation, in the same film. The temperature dependence of the resonance frequency, f(T), was then systematically studied. By using Chang's inductive formula and taking a functional form (λ(5K)/λ(T)) 2 = 1 - (T/Tc)2 at T < 0.6Tc, the London penetration depths λ(5K) for various oxygen contents at 5K were obtained, respectively. Finally, it allows us to test the Uemura relation 1/λ2(5K) ∝ Tc from the over- to the underdoped regime in the same sample.

原文English
頁(從 - 到)133-138
頁數6
期刊Physica C: Superconductivity and its applications
415
發行號3
DOIs
出版狀態Published - 15 10月 2004

指紋

深入研究「Microwave properties of a Y0.7Ca0.3Ba 2Cu3O7-δ microstrip ring resonator with various hole concentrations」主題。共同形成了獨特的指紋。