Mesoporous nickel ferrites with spinel structure prepared by an aerosol spray pyrolysis method for photocatalytic hydrogen evolution

Submicron-sized mesoporous nickel ferrite (NiFe₂O₄) spheres were prepared by an aerosol spray pyrolysis method using Pluronic F127 as a structure-directing agent, and their photocatalytic performance for hydrogen (H₂) evolution was examined in an aqueous MeOH solution by visible light irradiation (λ > 420 nm). The structure of the spherical mesoporous nickel ferrites was studied by transmission electron microscopy, powder X-ray diffraction, and N₂ adsorption-desorption isotherm measurements. Mesoporous NiFe₂O₄ spheres of high specific surface area (278 m² g^-1) with a highly crystalline framework were prepared by adjusting the amount of structure-directing agent and the calcining condition. High photocatalytic activity of mesoporous NiFe₂O₄ for H₂ evolution from water with methanol was achieved due to the combination of high surface area and high crystallinity of the nickel ferrites.