Low-pressure crystallization of sol-gel-derived PbZr 0.52 Ti 0.48 O 3 thin films at low temperature for low-voltage operation

Ding Yeong Wang*, Chao-Hsin Chien, Chun Yen Chang, Ching Chich Leu, Jung Yen Yang, Shiow Huey Chuang, Tiao Yuan Huang

*此作品的通信作者

研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)

摘要

The properties of sol-gel-derived 120-nm PbZr0.52Ti0.48O3 thin films crystallized in low-pressure O2 ambient at 500 °C have been investigated. It is found that PbZr0.52Ti0.48O3 films crystallized in low-pressure oxygen ambient exhibit higher remanent polarization as well as a lower coercive field, compared to those annealed in O2 atmosphere. The remanent polarization (i.e., 2Pr) for samples annealed in 60 mbar O2 ambient is as high as 36 μC/cm2, and the coercive field (2EC) is 99.9 kV/cm at an applied voltage of 2 V. The improvement of P-E hysteresis loops by low-pressure oxygen annealing is ascribed to less incorporation of oxygen and other residues in the resultant PbZr0.52Ti0.48O3 films, since the reductions in the amount of these residual species are beneficial for the complete transformation of the perovskite structure. The reductions in oxygen content and amounts of other residues such as CO2 and H2O are confirmed based on Auger depth profiles and thermal desorption spectra (TDS), respectively.

原文English
頁(從 - 到)2756-2758
頁數3
期刊Japanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
42
發行號5 A
DOIs
出版狀態Published - 5月 2003

指紋

深入研究「Low-pressure crystallization of sol-gel-derived PbZr 0.52 Ti 0.48 O 3 thin films at low temperature for low-voltage operation」主題。共同形成了獨特的指紋。

引用此