Laser-assisted chemical vapor deposition of InN on Si(100)

Y. Bu, L. Ma, Ming-Chang Lin

研究成果: Article同行評審

55 引文 斯高帕斯(Scopus)


Laser-assisted chemical vapor deposition of InN on Si(100) using HN3 and trimethyl indium (TMXn) with and without 308-nm photon excitation has been studied with x-ray photoelectron spectroscopy (XPS), ultraviolet photoelectron spectroscopy (UPS), and scanning electron microscopy (SEM). Without 308mm excimer laser irradiation, no InN him was built on the surface under the present low-pressure conditions. When the photon beam was introduced, InN films with In:N atomic ratio of LQiO.l and a thickness of more than 20 A (the limit of the electron escaping depth for the In 3d x-ray photoelectrons) were formed at temperatures of 300–700 K. The He ii UP spectra taken from these InN films agree well with the result of a pseudopotential calculation for the InN valence band. Our XPS measurements indicate a three-dimensional (3D) island growth of InN on Si(100) at 700 K, which is confirmed by the SEM images. Although the SEM images taken from the same samples with 2000 X magnification showed very smooth InN films, InN islands of about 100 nm in diameter could be clearly observed with a magnification of 20 000 X, In contrast, the InN film grown at 300 K showed valleys of uncovered substrate instead of InN islands. These uncovered substrate areas, corresponding to about 5% of the surface exposed to the probing x-ray radiation, probably result from incomplete decomposition of In-C bonds and poor diffusion kinetics at this temperature. Above 800 K5 dissociation and desorption of In- and N- containing species occurred and thus no InN film was formed on the surface.

頁(從 - 到)2931-2937
期刊Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films
出版狀態Published - 1 1月 1993


深入研究「Laser-assisted chemical vapor deposition of InN on Si(100)」主題。共同形成了獨特的指紋。