Ion-beam-induced metastable Pt 2 Si 3 phase. III. Structure and diffusion in amorphous Pt 2 Si 3

J. F. Graczyk*, King-Ning Tu, B. Y. Tsaur, J. W. Mayer

*此作品的通信作者

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)

摘要

We have used electron microscopy, scanning electron diffraction, and structure modeling techniques to investigate crystallization behavior and structure of ion-mixed and codeposited films of Pt-Si of various compositions deposited on Si and on NaCl. We have determined that the amorphous alloys of ion-mixed Pt 2 Si 3 have lateral compositional fluctuations on the atomic scale of 80-160 Å in diameter. We show that the amorphous phase of Pt 2 Si 3 is a new phase which cannot be fully described by the simple binary dense random packing of hard spheres model (DRPHS). We propose, but do not prove unequivocably, that the amorphous structure can be described by a DRPHS model with lateral compositional fluctuations on the atomic scale of 80-160 Å, which contains very small nuclei on the order of 5-7 Å in size. We further propose that these nuclei have a composition exactly equal to the metastable crystalline Pt 2 Si 3 phase, and that they cannot grow without a high temperature annealing because of the surrrounding amorphous material of slightly different composition. We find a long range diffusion process for amorphous Pt 2 Si 3 at temperatures below crystallization. The activation energy for the process is 1.56±0.2 eV, with an average 〈D〉=2.0×10 -15 cm 2 /sec at 385 °C. The process can relax and homogenize the amorphous structure by atomic displacements over a distance of 80-160 Å, and is probably possible because of micropores in the film. The structures of Pt 62 Si 38 and Pt 2 6 Si 74 on NaCl were amorphous, while that of Pt 80 Si 20 was microcrystalline.

原文English
頁(從 - 到)6772-6780
頁數9
期刊Journal of Applied Physics
53
發行號10
DOIs
出版狀態Published - 1 十二月 1982

指紋

深入研究「Ion-beam-induced metastable Pt <sub>2</sub> Si <sub>3</sub> phase. III. Structure and diffusion in amorphous Pt <sub>2</sub> Si <sub>3</sub>」主題。共同形成了獨特的指紋。

引用此