Interfacial reactions between Ti and Y2O3/Ca4Ti3O10 composites

Ming Wei Lu, Kun Lin Lin, Chien Cheng Lin*

*此作品的通信作者

    研究成果: Article同行評審

    1 引文 斯高帕斯(Scopus)

    摘要

    In titanium casting, the interfacial reactions between selected Y2O3/Ca4Ti3O10 composites in contact with titanium at 1600°C for 30 minutes in an argon environment were characterized using X-ray diffraction, scanning electron microscopy, and analytical transmission electron microscopy. Before contact with titanium, reaction phases of the Y2O3/Ca4Ti3O10 composites formed through hot pressing at 1500°C or annealing at 1600°C. These phases were identified as Ca4Ti3O10, Y2O3, and minor amounts of CaO. The amount of Ca4Ti3O10 in the composites gradually decreased as the amount of Y2O3 increased. When the Y2O3/Ca4Ti3O10 composites were in contact with titanium, a reaction layer of α-Ti and Y2O3 was formed near the interface of the composite side. Large amounts of calcium and oxygen were expelled toward the composite side from Ca4Ti3O10 near the interface to form CaO, which precipitated in the Ca4Ti3O10 and Y2O3 phases. Furthermore, no reaction phases were detected in titanium. Ca4Ti3O10 and Y2O3 can function as diffusion barrier layers to effectively suppress the diffusion of oxygen into titanium.

    原文English
    期刊International Journal of Applied Ceramic Technology
    17
    發行號3
    DOIs
    出版狀態Published - 五月 2020

    指紋

    深入研究「Interfacial reactions between Ti and Y<sub>2</sub>O<sub>3</sub>/Ca<sub>4</sub>Ti<sub>3</sub>O<sub>10</sub> composites」主題。共同形成了獨特的指紋。

    引用此