Improving Optical and Electrical Characteristics of GaN Films via 3D Island to 2D Growth Mode Transition Using Molecular Beam Epitaxy

Molecular beam epitaxy (MBE) is demonstrated as an excellent growth technique for growing a low-defect GaN channel layer, which is crucial for controlling vertical leakage current and improving breakdown voltage (BV) in GaN-based high-electron mobility transistors (HEMTs). The 3D islands to 2D growth mode transition approach was induced by modulating substrate growth temperature (Tsub), displaying an overall improvement in film quality. A comprehensive investigation was conducted into the effects of Tsub on surface morphologies, crystal quality, and the optical and electrical properties of GaN films. Optimal results were achieved with a strain-relaxed GaN film grown at 690 °C, exhibiting significantly improved surface characteristics (root-mean-square roughness, Rq = 0.3 nm) and impressively reduced edge dislocations. However, the film with the smoothest surface roughness, attributed to the effect of the Ga-rich condition, possessed a high surface pit density, negatively affecting optical and electrical properties. A reduction in defect-related yellow emission further confirmed the enhanced crystalline quality of MBE GaN films. The optimized GaN film demonstrated outstanding electrical properties with a BV of ~1450 V, surpassing that of MOCVD GaN (~1180 V). This research significantly contributes to the advancement of MBE GaN-based high electron mobility transistor (HEMT) applications by ensuring outstanding reliability.