Highly efficient white organic electroluminescent devices based on tandem architecture

Chan Ching Chang*, Jenn-Fang Chen, Shiao Wen Hwang, Chin H. Chen

*此作品的通信作者

研究成果: Article同行評審

186 引文 斯高帕斯(Scopus)

摘要

Two types of tandem organic light-emitting diodes (OLEDs) with white-light emission have been developed by using Mg:Al q3 W O3 as the interconnecting layer. While the Commission Internationale d'Eclairage (CIE) coordinates of the tandem device with individual blue- and yellow-emitting OLEDs was sensitive to the viewing angle and the operating time, the tandem device connecting two white-emitting OLEDs was considerably less. At an optimal W O3 thickness of 5 nm, the tandem two-unit device produced three higher luminance efficiency than that expected of a single-unit device. A maximum efficiency of 22 cdA was achieved by the tandem device comprised of two white-fluorescent OLEDs, and the projected half-life under the initial luminance of 100 cd m2 was over 80 000 h.

原文English
文章編號253501
頁(從 - 到)1-3
頁數3
期刊Applied Physics Letters
87
發行號25
DOIs
出版狀態Published - 2005

指紋

深入研究「Highly efficient white organic electroluminescent devices based on tandem architecture」主題。共同形成了獨特的指紋。

引用此