High-quality and highly-transparent AlN template on annealed sputter-deposited AlN buffer layer for deep ultra-violet light-emitting diodes

Chia-Yen Huang, Pei Yu Wu, Kai Shiang Chang, Yun Hsiang Lin, Wei Chih Peng, Yem Yeu Chang, Jui Ping Li, Hung Wei Yen, Yew-Chuhg Wu, Hideto Miyake, Hao-Chung Kuo

研究成果: Article同行評審

40 引文 斯高帕斯(Scopus)

摘要

A high-quality and highly-transparent AlN template was prepared by regrowth on a sputter-deposited AlN buffer layer. The buffer layer was thermally annealed and then underwent AlN regrowth in metalorganic chemical vapor deposition (MOCVD). The peakwidth of (002) and (102) plane x-ray rocking curve was 104 arcsec and 290 arcsec, respectively, indicating a threading dislocation density <5.0 × 10 8 cm −2 . Dislocations were reduced via grain growth and morphological evolution. The absence of carbon impurity source in sputter deposition also resulted in an improved transparency. According to transmission and reflection measurements, the absorption rate of λ=280 nm emission propagating through the template was less than 6%.

原文American English
文章編號055110
頁(從 - 到)1-6
頁數6
期刊AIP Advances
7
發行號5
DOIs
出版狀態Published - 1 5月 2017

指紋

深入研究「High-quality and highly-transparent AlN template on annealed sputter-deposited AlN buffer layer for deep ultra-violet light-emitting diodes」主題。共同形成了獨特的指紋。

引用此