Grain-Boundary Magnetoresistance of CrO2 Films Grown on TiO 2-Buffered LaAlO3 Substrates

S. J. Liu*, Jenh-Yih Juang, Kaung-Hsiung Wu, T. M. Uen, Y. S. Gou, Jiunn-Yuan Lin


研究成果: Article同行評審

4 引文 斯高帕斯(Scopus)


The magnetic and magnetotransport properties of predominantly (110)-oriented CrO2 films grown on TiO2-buffered LaAlO3 substrates were investigated. The atomic force microscopic images revealed that the as-grown CrO2 films are granular. The magnetic measurements indicated that in-plane coercive fields are about 60 Oe and 100 Oe at 300 K and 7 K, respectively. The as-grown films are semiconductive below 75 K; a magnetoresistance with a ΔR/R0 ratio of -13 % in a magnetic field of 5 T was observed at 5 K, which is absent in high-quality epitaxial films. The coincidence between the coercive field and the peaks of the magnetoresistive loop measured at low temperatures indicates that spin-dependent scattering plays a crucial role in the transport properties.

原文American English
頁(從 - 到)406-413
期刊Chinese Journal of Physics
出版狀態Published - 1 8月 2003


深入研究「Grain-Boundary Magnetoresistance of CrO2 Films Grown on TiO 2-Buffered LaAlO3 Substrates」主題。共同形成了獨特的指紋。