GaN-based light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques

Ray-Hua Horng*, Kuan Fu Pan, Chia En Lee, Shao Hua Hung, Wen Yu Lin, Ying Yong Su, Chiao Chih Yang, Dong Sing Wuu

*此作品的通信作者

研究成果: Paper同行評審

摘要

This work reports a p-side-down GaN/mirror/Si light-emitting diode (LED) for vertical current injection fabricated by laser lift-off and wafer bonding techniques. The large area (1 mm×1 mm) GaN/mirror/Si LED with a platinum mirror presents a luminance intensity of 1456 mcd (@350mA) with a forward voltage of 3.96 V. The luminance intensity is two times in magnitude as compared with that of the original GaN/sapphire LED (456mcd, 4.2V @350mA). When the driving current increased to 1 A, the luminance intensity of GaN/mirror/Si LED achieved 2876 mcd, which was 2.8 times in magnitude as compared with that of the original planar GaN/sapphire LED (@1019mcd). These results indicate that the wafer bonding and laser lift-off techniques do not adversely affect the current-voltage characteristics of the LEDs. Furthermore, under high current injection, the GaN/mirror/Si LED presents the better performance due to the Si heat sink.

原文English
頁面140-151
頁數12
出版狀態Published - 1 十二月 2005
事件207th ECS Meeting - Quebec, Canada
持續時間: 16 五月 200520 五月 2005

Conference

Conference207th ECS Meeting
國家/地區Canada
城市Quebec
期間16/05/0520/05/05

指紋

深入研究「GaN-based light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques」主題。共同形成了獨特的指紋。

引用此