Formation of omega and Ti2Ni phases in a residual Ti-Ni-Ti multilayer between stainless steel and zirconia after bonding at 1173 K

Shen Hung Wei, Chien-Cheng Lin*

*此作品的通信作者

研究成果: Article同行評審

摘要

Stainless steel (316L) and 8 mol pct Y2O3-stabilized zirconia (8Y-ZrO2) were bonded using a Ti-Ni-Ti multilayer at 1173 K (900 °C) for 1 h. Cross-sectional transmission electron microscopy specimens were prepared by an innovative focused ion beam plus lift-out technique. In addition to acicular α-Ti, the dissolution of Fe, Cr, and Ni diffusing outwards from 316L into β-Ti led to the precipitation of the omega (ω) phase with different variants in the residual Ti foil between 316L and Ni. The ω-phase was not found in the residual Ti foil between Ni and 8Y-ZrO2, while Ti2Ni precipitates were precipitated in some α-Ti grains owing to the exclusion of Ni from the β-Ti.

原文English
頁(從 - 到)609-619
頁數11
期刊Philosophical Magazine Letters
94
發行號10
DOIs
出版狀態Published - 3 十月 2014

指紋

深入研究「Formation of omega and Ti<sub>2</sub>Ni phases in a residual Ti-Ni-Ti multilayer between stainless steel and zirconia after bonding at 1173 K」主題。共同形成了獨特的指紋。

引用此