Flower-like nanosheets FeCo2O4 for application in supercapacitor and dye-sensitized solar cell

Farish Irfal Saaid, Muhd Firdaus Kasim, Chien Chih Yang, Amit Kumar, Tseung Yuen Tseng, Tan Winie*

*此作品的通信作者

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

Four different iron cobaltite (FeCo2O4) structures namely nanoneedles, nanorods, nanosheets and microcubes have been obtained by varying the duration of hydrothermal reaction. The dependence of electrochemical properties on the FeCo2O4 structures has been investigated. The FeCo2O4 nanosheet have the highest specific capacitance (Csp), followed by nanorods, nanoneedles and microcubes. The highest Csp of FeCo2O4 nanosheets is attributed to its highest specific surface area and pore volume. A solid-state asymmetric FeCo2O4 nanosheet/polyvinyl alcohol—potassium hydroxide/reduced graphene oxide supercapacitor was fabricated. The supercapacitor exhibits maximum power density of 3202 W kg−1 and maximum energy density of 24.5 Wh kg−1. It demonstrates 70% capacitance retention after 3000 cycles. The poly(vinylidene fluoride-co-hexafluoropropylene)/propylene carbonate/1,2-dimethoxyethane/1-methyl-3-propyl imidazolium iodide/sodium iodide/iodine/4-tert-butylpyridine/guanidine thiocyanate electrolytes were assembled into dye-sensitized solar cells (DSSCs) with FeCo2O4 nanosheets or platinum as the counter electrodes. DSSC with FeCo2O4 nanosheets counter electrode shows an efficiency of 6.04%.

原文English
頁(從 - 到)3648-3669
頁數22
期刊Journal of Materials Science: Materials in Electronics
33
發行號7
DOIs
出版狀態Published - 3月 2022

指紋

深入研究「Flower-like nanosheets FeCo2O4 for application in supercapacitor and dye-sensitized solar cell」主題。共同形成了獨特的指紋。

引用此