Facile and surfactant-free route to mesoporous silica-based adsorbents from TFT-LCD industrial waste powder for CO2 capture

Liang-Yi Lin, Hsun-Ling Bai*

*此作品的通信作者

研究成果: Article同行評審

24 引文 斯高帕斯(Scopus)

摘要

A surfactant-free preparation of mesoporous silica spherical particles, MSPs was developed using sodium silicate extracted from TFT-LCD industrial waste powder via aerosol spray route in this study. Inorganic acids including hydrochloric acids and nitric acids were employed to acidify the silicate supernatant to form activated silica precursors and the influence of acids in the activated silica precursors was studied. The MSPs(HNO3), which was synthesized in the presence of nitric acids exhibited high surface area (776 m2/g), mesopore size (5.3 nm) as well as large pore volume (1.15 cm3/g) and it was further applied as a support of adsorbent for CO2 capture. It was demonstrated that tetraethylenepentamine (TEPA)-impregnated MSPs(HNO3) adsorbent presents advantages of convenient synthesis, low cost and high adsorption performance (122 mg-CO 2/g-adsorbent), which was superior to those of TEPA-SBA-15 and TEPA-MCM-41 manufactured from pure silica chemicals under the same test conditions. The results suggested that low-cost MSPs(HNO3) prepared using silicate solution from TFT-LCD waste powder via spray approach can be promising CO2 adsorbents. This novel process could also be employed for further extensible to other kinds of Si-related industrial wastes and benefit in large-scale production of highly valuable silica-based sorbents for environmental protection applications.

原文American English
頁(從 - 到)266-273
頁數8
期刊Microporous and Mesoporous Materials
170
DOIs
出版狀態Published - 4月 2013

指紋

深入研究「Facile and surfactant-free route to mesoporous silica-based adsorbents from TFT-LCD industrial waste powder for CO2 capture」主題。共同形成了獨特的指紋。

引用此