Fabrication of centimeter-scale MAPbBr3 light-emitting device with high color purity

Shih Jung Chang, Liang Chen Li, Tzu Hsin Hong, Muthaiah Shellaiah, Kien-Wen Sun*

*此作品的通信作者

研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)

摘要

In this study, 3 cm × 3 cm organometallic halide perovskite (MAPbBr3) nanocrystalline thin film and light-emitting diodes (LEDs) were synthesized and fabricated using a combined thermal evaporation and spin-coating technique. PEDOT:PSS(Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate)) and TPBi(2,2′,2"-(1,3,5-Benzinetriyl)-tris(1-phenyl-1- H-benzimidazole)) were used as the hole and electron transport layers for the LEDs, respectively. The structural, photophysical, electronic, and electroluminescent properties of the devices were measured and characterized. The p-i-n device showed a turn-on voltage of approximately 1.5 V, with electroluminescence centered at 535 nm at a full width at half maximum (FWHM) of 14 nm. The device displayed high color purity, an external quantum efficiency, and a maximum luminance of 100%, 1.86%, and 1610 cd/m2, respectively. Results demonstrated the advantages of combining thermal evaporation and solution process in producing larger-area perovskite display and lighting devices.

原文English
文章編號105931
期刊Organic Electronics
86
DOIs
出版狀態Published - 11月 2020

指紋

深入研究「Fabrication of centimeter-scale MAPbBr3 light-emitting device with high color purity」主題。共同形成了獨特的指紋。

引用此