Exposure assessment of nano-sized and respirable particles at different workplaces

Chuen-Tinn Tsai*, Cheng Yu Huang, Sheng Chieh Chen, Chi En Ho, Cheng Hsiung Huang, Chun Wan Chen, Cheng Ping Chang, Su Jung Tsai, Michael J. Ellenbecker

*此作品的通信作者

研究成果: Article同行評審

72 引文 斯高帕斯(Scopus)

摘要

In this study, nanoparticle (NP, diameter < 100 nm) and respirable particles measurements were conducted at three different nanopowder workplaces, including the mixing area of a nano-SiO2- epoxy molding compound plant (primary diameter: 15 nm), bagging areas of a nano-carbon black (nano- CB) (primary diameter: 32 nm) and a nano-CaCO3 (primary diameter: 94 nm) manufacturing plant. Chemical analysis of respirable particle mass (RPM) and NPs was performed to quantify the content of manufactured nanoparticles in the collected samples. Nanopowder products obtained from the plants were used in the laboratory dustiness testing using a rotating drum tester to obtain particle mass and number distributions. The obtained laboratory data were then used to elucidate the field data. Both field and laboratory data showed that NP number and mass concentrations of manufactured materials were close to the background level. Number concentration was elevated only for particles with the electrical mobility diameter > 100 nm during bagging or feeding processes, unless there were combustionrelated incidental sources existed. Large fraction of nanomaterials was found in the RPM due to agglomeration of nanomaterials or attachment of nanomaterials to the larger particles. From this study, it is concluded that RPM concentration measurements are necessary for the exposure assessment of nanoparticles in workplaces.

原文English
頁(從 - 到)4161-4172
頁數12
期刊Journal of Nanoparticle Research
13
發行號9
DOIs
出版狀態Published - 9月 2011

指紋

深入研究「Exposure assessment of nano-sized and respirable particles at different workplaces」主題。共同形成了獨特的指紋。

引用此