Efficiency improvement of near-ultraviolet InGaN LEDs using patterned sapphire substrates

Woei Kai Wang*, Dong Sing Wuu, Shu Hei Lin, Pin Han, Ray-Hua Horng, Ta Cheng Hsu, Donald Tai Chan Huo, Ming Jiunn Jou, Yuan Hsin Yu, Aikey Lin

*此作品的通信作者

研究成果: Article同行評審

75 引文 斯高帕斯(Scopus)

摘要

The use of conventional and patterned sapphire substrates (PSSs) to fabricate InGaN-based near-ultraviolet (410 nm) light-emitting diodes (LEDs) was demonstrated. The PSS was prepared using a periodic hole pattern (diameter: 3 μm; spacing: 3 μn) on the (0001) sapphire with different etching depths. From transmission-electron-microscopy and etch-pit-density studies, the PSS with an optimum pattern depth (Dh = 1.5 μm) was confirmed to be an efficient way to reduce the thread dislocations in the GaN microstructure. It was found that the output power increased from 8.6 to 10.4 mW, corresponding to about 29% increases in the external quantum efficiency. However, the internal quantum efficiency (20 mA) was about 36% and 38% for the conventional and PSS LEDs, respectively. The achieved improvement of the output power is not only due to the improvement of the internal quantum efficiency upon decreasing the dislocation density, but also due to the enhancement of the extraction efficiency using the PSS. Finally, better long-time reliability of the PSS LED performance was observed.

原文English
頁(從 - 到)1403-1409
頁數7
期刊IEEE Journal of Quantum Electronics
41
發行號11
DOIs
出版狀態Published - 1 11月 2005

指紋

深入研究「Efficiency improvement of near-ultraviolet InGaN LEDs using patterned sapphire substrates」主題。共同形成了獨特的指紋。

引用此