Effects of zirconium oxide on the sintering of SrCe1-xZrxO3-δ (0.0 蠆 x 蠆 0.5)

Kai Ti Hsu*, Jason Shian Ching Jang, Yu Jing Ren, Pei Hua Tsai, Chuan Li, Chung Jen Tseng, Jing Chie Lin, Chi Shiung Hsi, I. Ming Hung


研究成果: Article同行評審

8 引文 斯高帕斯(Scopus)


SrCe1-xZrxO3-δ (0.0 蠆 x 蠆 0.5) proton-conducting oxides had been successfully prepared using a solid state reaction method. In this study, the relationships between the Zr contents and microstructures, shrinkages, and sintering of these SrCe1-xZrxO3-δ (0.0 蠆 x 蠆 0.5) were systemically studied by using X-ray Diffraction, Scanning Electron Microscopy, and Thermal dilatometer analysis (TDA). The XRD results showed that no second phase could be found from the 1500 °C sintered SrCe1-xZrxO3-δ. The SEMs shows that the porosities of sintered SrCe1-xZrxO3-δ increased with increasing the Zr contents. The largest porosity about 27.53% could be obtained at the SrCe0.6Zr0.4O3-δ ceramics sintered at 1500 °C for 2 h in the SrCe1-xZrxO3-δ ceramics. According to the sintering behaviour and properties characterizations, a flat HTM with porous supporting layers of SrCe0.6Zr0.4O3-δ and SrZrO3 was fabricated by constrained sintering. Therefore, the SrCe0.6Zr0.4O3-δ ceramic is suggested to be a potential support layer material for HTM applications.

頁(從 - 到)S491-S495
期刊Journal of Alloys and Compounds
出版狀態Published - 15 1月 2015


深入研究「Effects of zirconium oxide on the sintering of SrCe1-xZrxO3-δ (0.0 蠆 x 蠆 0.5)」主題。共同形成了獨特的指紋。