Effects of the growth temperature on structural and electrical properties of AlN/GaN heterostructures grown by metal organic chemical vapor deposition

Xia Xi Zheng, Chun-Hsiung Lin, Daisuke Ueda, Edward Yi Chang*

*此作品的通信作者

研究成果: Article同行評審

5 引文 斯高帕斯(Scopus)

摘要

In this paper, we present the dependence of structural and electrical properties of AlN/GaN heterostructure on the growth temperature on sapphire substrates by metal organic chemical vapor deposition. The results revealed that higher Ga incorporation (~47%) and higher trench density on the surface of AlN barrier layer when grown at 1125 °C. However, further decreasing the AlN growth temperature to 500 °C results in the lower Ga incorporation (~5%), higher dislocation density, 3D island growth and larger tensile strain of AlN barrier layer. Degradation of structural properties and surface morphologies AlN barrier layer results in the higher resistivity of 2-dimensional electron gas transport properties. Low sheet resistance (255.45 Ω/sq), high free carrier electron density (2.86 × 1013 cm−2), simultaneously maintaining low surface roughness and high crystal quality of AlN barrier were achieved at optimized growth temperature around 800 °C.

原文American English
文章編號138228
頁(從 - 到)1-5
頁數5
期刊Thin Solid Films
709
DOIs
出版狀態Published - 1 9月 2020

指紋

深入研究「Effects of the growth temperature on structural and electrical properties of AlN/GaN heterostructures grown by metal organic chemical vapor deposition」主題。共同形成了獨特的指紋。

引用此