Effects of growth temperature on In N / Ga N nanodots grown by metal organic chemical vapor deposition

Wen-Hao Chang*, Wen Cheng Ke, Shu Hung Yu, Lin Lee, Ching Yu Chen, Wen Che Tsai, Hsuan Lin, Wu-Ching Chou, Ming Chih Lee, Wei-Kuo Chen

*此作品的通信作者

研究成果: Article同行評審

19 引文 斯高帕斯(Scopus)

摘要

InN nanodots grown on GaN by metal organic chemical vapor deposition using conventional growth mode as well as flow-rate modulation epitaxy at various growth temperatures (550-730 °C) were investigated. We found that different precursor injection schemes together with the effect of growth temperatures greatly influenced the surface morphology of InN nanodots and their photoluminescence (PL) properties. The sample grown at around 650 °C showed the highest growth rate. For samples grown at higher temperatures, the residual carrier concentration was reduced and the PL efficiency was improved. Furthermore, we found that the growth of InN nanodots is still sustainable even at a temperature higher than 700 °C while retaining their optical quality.

原文English
文章編號104306
頁(從 - 到)1-7
頁數7
期刊Journal of Applied Physics
103
發行號10
DOIs
出版狀態Published - 15 5月 2008

指紋

深入研究「Effects of growth temperature on In N / Ga N nanodots grown by metal organic chemical vapor deposition」主題。共同形成了獨特的指紋。

引用此