Effect of Ti substitution on the electrochemical properties of LaCr1−xTi xO3+0.5x (x = 0–0.15)

Chia Kan Hao, Chia Fen Tsai, Chi-Shen Lee*

*此作品的通信作者

    研究成果: Article同行評審

    2 引文 斯高帕斯(Scopus)

    摘要

    Perovskite compound LaCr1−xTixO3+0.5x (x = 0–0.15) was synthesized from an EDTA-chelating precursor solution at T < 800 °C, a temperature lower than that of the conventional solid-state method. Structural properties were determined at room temperature using X-ray powder diffraction and the lattice parameter decreased with increasing proportion of Ti. LaCr1−xTixO3+0.5x was chemically stable under a H2 atmosphere at 900 °C. Both electrical and ionic conductivity increased with increasing proportion of doped Ti, indicative of a p-type semiconductor. An Arrhenius-like behavior was observed, and the optimized bulk electrical conductivity was 0.107 S cm−1 for LaCr0.85Ti0.15O3.075 at 850 °C. X-ray photoelectron spectra indicate that the effect of the concentration of charge carrier on conductivity is closely related to the oxidation states of ions. The maximum power density reaches as high as 210 mW cm−2 at 800 °C for SOFC with LaCr1−xTixO3+0.5x (x = 0.15) anode. Graphical Abstract: Ti-substituted perovskite materials LaTixCr1−xO3+0.5x (x = 0–0.15) show enhanced electronic and ionic conductivity with increasing proportion of doped Ti.[Figure not available: see fulltext.]

    原文English
    頁(從 - 到)394-402
    頁數9
    期刊Journal of Sol-Gel Science and Technology
    78
    發行號2
    DOIs
    出版狀態Published - 1 五月 2016

    指紋

    深入研究「Effect of Ti substitution on the electrochemical properties of LaCr<sub>1−x</sub>Ti<sub> x</sub>O<sub>3+0.5x</sub> (x = 0–0.15)」主題。共同形成了獨特的指紋。

    引用此