Dramatic reduction of gate leakage current in 1.61 nm HfO2 high-k dielectric poly-silicon gate with Al2O3 capping layer

Chih Wei Yang, Yean Kuan Fang*, Chien Hao Chen, Wen De Wang, Tin Yu Lin, Ming Fang Wang, Tuo-Hung Hou, Juing Yi Cheng, Liang Gi Yao, Shyh Chang Chen, Chen Hua Yu, Mong Song Liang

*此作品的通信作者

研究成果: Article同行評審

6 引文 斯高帕斯(Scopus)

摘要

The electrical properties of poly-silicon gate MOS capacitors with HfO2 gate dielectric, with and without Al2O3 capping layer, were investigated. Without the capping layer, the experimental results show that an unacceptably high gate leakage current due to the interaction between HfO2 and poly-silicon was observed; while with a thin Al2O3 layer capping on 1.61 nm equivalent oxide thickness (EOT) HfO2 dielectric the gate leakage current density can be reduce to approximately 10-7 A/cm2, which is nearly seven orders (107) in magnitude lower than that of using pure oxide with identical EOT.

原文English
頁(從 - 到)1223-1225
頁數3
期刊Electronics Letters
38
發行號20
DOIs
出版狀態Published - 26 9月 2002

指紋

深入研究「Dramatic reduction of gate leakage current in 1.61 nm HfO2 high-k dielectric poly-silicon gate with Al2O3 capping layer」主題。共同形成了獨特的指紋。

引用此