Diffusion of oxygen in superconducting YBa2Cu3O7- ceramic oxides

King-Ning Tu*, N. C. Yeh, S. I. Park, C. C. Tsuei

*此作品的通信作者

研究成果: Article同行評審

210 引文 斯高帕斯(Scopus)

摘要

We have used in situ resistivity measurements to monitor the diffusion of oxygen in and out of the ceramic oxide YBa2Cu3O7-. The study of out-diffusion of oxygen was carried out by annealing the oxide in ambient helium at constant heating rates and at constant temperatures. The rate of out-diffusion of oxygen has been found to be independent of , and the resistivity changes linearly with time during isothermal anneals. Assuming that the rate of out-diffusion is surface reaction limited, we have determined a surface barrier of 1.7 eV. The study of in-diffusion of oxygen was performed by annealing the oxygen-deficient oxide (=0.38) in ambient oxygen. The in-diffusion rate was found to depend strongly on ; we have determined the activation energies of the process at =0.38 and =0 to be 0.5 eV and 1.3 eV, respectively. The diffusivity of oxygen for =0 has been determined to be D=0.035 exp(-1.3eV/kT) cm2/sec. Combining the kinetic data and published structural information, we have examined a vacancy mechanism and a twinning mechanism for anisotropic diffusion of oxygen in the CuO layer between the BaO layers.

原文English
頁(從 - 到)304-314
頁數11
期刊Physical Review B
39
發行號1
DOIs
出版狀態Published - 1 1月 1989

指紋

深入研究「Diffusion of oxygen in superconducting YBa2Cu3O7- ceramic oxides」主題。共同形成了獨特的指紋。

引用此