Comparative study between conventional and microwave sintered lead-free BNKT ceramics

Pin Yi Chen*, Chen Chia Chou, Tseung-Yuen Tseng, Haydn Chen


研究成果: Conference article同行評審

6 引文 斯高帕斯(Scopus)


Lead free [(1-x)Bi0.5Na0.5TiO3-(x)Bi0.5K0.5TiO3] ceramics with x = 0.18 were prepared by using microwave sintering technique. XRD of these ceramics show co-existence of tetragonal and rhombohedral phases. Smaller grain size and more uniform microstructure were observed in microwave sintered sample. It might result from different diffusion mechanism. The activation energy of grain growth was calculated. The results display in microwave sintered sample is lower (167kJ/mol) than that for conventional one (260kJ/mol). It implies microwave sintered sample just need lower energy for densification. The remanent polarization and piezoelectric constants of microwave sintered samples are higher than that of conventional sintered samples. Relation among processing kinetics, microstructural characteristics and electrical properties was discussed.

頁(從 - 到)196-200
發行號1 PART 2
出版狀態Published - 1 12月 2009
事件6th Asian Meeting on Ferroelectrics, AMF-6 - Taipei, Taiwan
持續時間: 2 8月 20086 8月 2008


深入研究「Comparative study between conventional and microwave sintered lead-free BNKT ceramics」主題。共同形成了獨特的指紋。