Characterization and electrochemical properties of chromium-substituted pyrochlore Y2Ti2−xCr xO7−δ

Chia Kan Hao, Hao En Hung, Chi Shen Lee*

*此作品的通信作者

    研究成果: Article同行評審

    1 引文 斯高帕斯(Scopus)

    摘要

    Abstract: Pyrochlore oxides Y2Ti2−xCrxO7−δ have been investigated as electrolyte for solid oxide fuel cell. The as-prepared powder was synthesized by sol–gel method and characterized by powder X-ray diffraction, scanning electron microscope/energy-dispersive spectroscopy, inductively coupled plasma atomic emission spectroscopy, temperature-programmed reduction and AC impedance. Y2Ti2−xCrxO7−δ existed in single phase in a range of 0 < x ≤ 0.8, and the cell parameters decreased as the amount of Cr dopant increased. XPS analyses indicate that the average oxidation state of Crn+ ions decreased with the increased Cr content. Measurements of ionic conductivities induced that the optimized performance was observed at x = 0.2 with 0.01 S/cm at 700 °C due to an optimized condition of carrier concentration and carrier mobility. Graphical Abstract: Y2Ti2−xCrxO7−δ existed in single phase in a range of 0 < x ≤ 0.8 and the optimized performance of ionic conductivity was observed at x = 0.2 with 0.01 S/cm at 700 °C.[Figure not available: see fulltext.]

    原文English
    頁(從 - 到)428-435
    頁數8
    期刊Journal of Sol-Gel Science and Technology
    76
    發行號2
    DOIs
    出版狀態Published - 2 十一月 2015

    指紋

    深入研究「Characterization and electrochemical properties of chromium-substituted pyrochlore Y<sub>2</sub>Ti<sub>2−x</sub>Cr<sub> x</sub>O<sub>7−δ</sub>」主題。共同形成了獨特的指紋。

    引用此