Characteristics of YBa2Cu3O7 thin films deposited on substrates buffered by various TiO2 layers

Po Iem Lin*, Chia Wen Liu, Chich Chang Hsieh, Kaung-Hsiung Wu, Jenh-Yih Juang, Tseng Ming Uen, Jiunn-Yuan Lin, Yih Shung Gou

*此作品的通信作者

研究成果: Article同行評審

9 引文 斯高帕斯(Scopus)

摘要

Titanium nitride (TIN) and superconducting YBa2Cu3O7 (YBCO) thin films have been deposited sequentially on SrTiO3(STO)(100) substrates by in situ pulsed laser ablation. The TiN films were originally intended to serve as the lower contact electrode of the c-axis YBCO thin films. It was found that, although high-quality YBCO films could be obtained with the YBCO/TiN/STO(100) bilayer structure, the TiN(100) layer was oxidized which changed the structure into YBCO/TiO2/STO(100) during YBCO deposition. Comparative studies of depositing YBCO films directly onto a dc-sputtered TiO2/STO(100) template conventionally used in the selective epitaxial growth (SEG) process have, however, resulted in formation of a nonsuperconducting YBCO top layer. The characteristics of the resultant TiO2 layers obtained using various processes were analyzed to delineate the apparent discrepancies.

原文English
頁(從 - 到)L377-L379
期刊Japanese Journal of Applied Physics, Part 2: Letters
40
發行號4 B
DOIs
出版狀態Published - 15 4月 2001

指紋

深入研究「Characteristics of YBa2Cu3O7 thin films deposited on substrates buffered by various TiO2 layers」主題。共同形成了獨特的指紋。

引用此