Autothermal steam reforming of ethanol over La2Ce2-xRuxO7 (x=0-0.35) catalyst for hydrogen production

Sheng Feng Weng, Yun Hsin Wang, Chi-Shen Lee*


    研究成果: Article同行評審

    34 引文 斯高帕斯(Scopus)


    Pyrochlore phases solid solutions, La2Ce2-xRuxO7 (x=0-0.35) were prepared with a sol-gel process and used as catalysts for the autothermal steam reforming of ethanol. The samples as prepared were characterized with powder X-ray diffraction (PXRD), X-ray photoelectron spectra (XPS), and temperature-programmed reduction (TPR). The XPS and TPR spectra revealed the effect of doped Run+ to oxidation states of La and Ce sites. The low temperature reduction ability and relative concentration of Ce4+ ions are increased as the cell-dimension decreased. Tests of catalytic activity showed that the reforming performance of La2Ce2-xRuxO7 catalysts was affected by the Ru/Ce loading ratio. For all catalysts, partial oxidation was favored at a large C/O composition; incomplete ethanol conversion was observed for C/O≥0.7. The optimized catalyst was La2Ce1.8Ru0.2O7 with hydrogen production rate (rH2) 2.01×10-3mols-1gcat -1 (autothermal temperature ∼600°C and 97% ethanol conversion at C/O=0.6). The catalyst exhibited stable rH2 over 26h of the reaction with ethanol conversion >95%. rH2 of the catalyst gradually decreased thereafter because LaAlO3 started to formed and affected catalytic process. For the catalyst, the Ru ions remained well dispersed before and after the AESR reaction.

    頁(從 - 到)359-366
    期刊Applied Catalysis B: Environmental
    出版狀態Published - 2 五月 2013


    深入研究「Autothermal steam reforming of ethanol over La2Ce2-xRuxO7 (x=0-0.35) catalyst for hydrogen production」主題。共同形成了獨特的指紋。