Aligned graphene platelets for the detection of crack extensions in nanocomposites

Po Chun Chuang, Jia-Lin Tsai*

*此作品的通信作者

研究成果: Article同行評審

1 引文 斯高帕斯(Scopus)

摘要

Nanocomposites with aligned graphene were fabricated and used to detect crack extension. Graphene were dispersed into epoxy resin through mechanical mixing followed by the sonication. To align the graphene, the graphene and epoxy mixture was subjected to an electrical field for 20 min. When the graphene loading was close to the percolation threshold (0.15 wt%), the network was established and the electrical conductivity of the nanocomposite dramatically increased. Three-point bending tests were conducted on single edge notch bending (SENB) specimens with the graphene aligned perpendicular to the loading direction. During the tests, the electrical resistance of the specimens was measured using a high-resistance meter. The results indicated that the resistance of the samples increased markedly prior to crack extension. Thus, aligned graphene can be employed to detect crack extensions.

原文American English
文章編號100833
期刊Composites Communications
27
DOIs
出版狀態Published - 10月 2021

指紋

深入研究「Aligned graphene platelets for the detection of crack extensions in nanocomposites」主題。共同形成了獨特的指紋。

引用此