Air-oxidation of an amorphous Fe70C10P10B5Mo5 alloy at 400–500 °C

W. Kai*, F. P. Cheng, Y. T. Chen, R. T. Huang, H. H. Huang, W. Zhang

*此作品的通信作者

研究成果: Article同行評審

11 引文 斯高帕斯(Scopus)

摘要

This research was conducted to demonstrate the oxidation behavior of an Fe70C10P10B5Mo5 amorphous ribbon investigated at 400–500 °C in dry air. The oxidation kinetics of the glassy alloy generally obeyed the parabolic-rate law with its oxidation rate constants steadily increasing with temperature. The oxidation rates of this alloy were slower than those of pure Fe and this indicated its better oxidation-resistant ability. The scale formed on the glassy alloy consisted mostly of a Fe2O3/Fe3O4 mixture, while minor amount of B2O3 was detected in the innermost scale.

原文English
頁(從 - 到)209-215
頁數7
期刊Journal of Alloys and Compounds
763
DOIs
出版狀態Published - 30 9月 2018