Aerosol processing of low-cost mesoporous silica spherical particles from photonic industrial waste powder for CO2 capture

Liang-Yi Lin, Hsun-Ling Bai*

*此作品的通信作者

研究成果: Article同行評審

24 引文 斯高帕斯(Scopus)

摘要

A novel mesoporous silica spherical particle, MSP (AS) was facilely prepared using photonic industrial waste powder as the silica source via salt-templated aerosol spray approach. As an alternative to expensive mesoporous silica materials in prior works, the obtained MSP (AS) possesses advantages of simple and rapid synthesis with low manufacturing costs. The characteristics of the MSP (AS) material were investigated by the XRD, N2 adsorption-desorption measurement, SEM, TEM and TG/DTG analyses. The results clearly demonstrated the presence of mesoporous siliceous material with high specific surface area (585m2/g), mesopore size (9.1nm) as well as large pore volume (1.24cm3/g). Furthermore, the MSP (AS) is evaluated as the support of adsorbent in terms of CO2 adsorption. It is observed that the amine-functionalized MSP (AS) adsorbent (TEPA-MSP (AS)) which possessed larger pore diameter and pore volume tends to have a higher adsorption capacity of 127mgCO2/gadsorbent. This is superior to those of TEPA-SBA-15 (117mgCO2/gadsorbent), TEPA-MCM-41 (112mgCO2/gadsorbent) and TEPA-NaY (96mgCO2/gadsorbent) under the same test condition. The results clearly suggest that the MSP (AS) synthesized using photonic industrial solid wastes via salt-templated aerosol route can be a potential and cost-effective adsorbent for CO2 capture.

原文American English
頁(從 - 到)215-222
頁數8
期刊Chemical Engineering Journal
197
DOIs
出版狀態Published - 15 7月 2012

指紋

深入研究「Aerosol processing of low-cost mesoporous silica spherical particles from photonic industrial waste powder for CO2 capture」主題。共同形成了獨特的指紋。

引用此