A study on improving the mechanical performance of carbon-fiber-reinforced cement

This study investigated several approaches for silane-removal from the surface of short carbon fiber bundles, and short carbon fibers uniformly dispersed in cement to produce a novel compound of carbon-fiber-reinforced cement. In order to facilitate the uniform distribution of short carbon fibers in the carbon-fiber-reinforced cement, it is necessary to remove the silane from the carbon fiber's surface. Short carbon fiber bundles were submerged into a pure water, sodium hydroxide solution, and acetic acid solution, and placed in high-temperature furnace used to remove silane from the carbon fiber surface. The results were observed under a scanning electron microscope to determine the level of silane removal from the surface, and an effective method for removing the silane was developed from among the several approaches. This method employed a pneumatic dispersion device to disperse carbon fibers then mixed in a high-early-strength cement which led to an excellent compressive and impact-resistance performance of carbon-fiber-reinforced cement. Final testing showed that the compressive strength and impact energy increased by 14.1% and 145%, respectively.