A novel tunable green- to yellow-emitting β-YFS:Ce 3+ phosphor for solid-state lighting

Yun Chen Wu, De Yin Wang, Teng-Ming Chen*, Chi-Shen Lee, Kuo Ju Chen, Hao-Chung Kuo

*此作品的通信作者

    研究成果: Article同行評審

    97 引文 斯高帕斯(Scopus)

    摘要

    A Ce 3+ -activated fluorosulfide phosphor (β-YFS:Ce 3+ ) was synthesized by solid-state reaction in a sealed tube. The crystal structure has been refined from the XRD profiles and there are two different crystallographic rare earth sites, namely, Y(1) and Y(2), where the Ce 3+ ions occupied. The emission band with a maximum at 495 nm of β-Y 0.99 Ce 0.01 FS phosphor was characterized by the 4f-5d transitions of Ce 3+ ion. With increasing Ce 3+ concentration, the emission variations were observed from 495 to 547 nm. When β-YFS:Ce 3+ phosphors were utilized to incorporate with n-UV/blue chip, greenish-white light with color rendering index of 65-77 were obtained. The results indicate that the tunable green- to yellow-emitting β-YFS:Ce 3+ can serve as a potential phosphor for incorporation in fabrication for solid-state lighting. The preparation, spectroscopic characterization, quantum efficiency, thermal-quenching behavior, and related LED device data are also presented.

    原文English
    頁(從 - 到)3195-3199
    頁數5
    期刊ACS Applied Materials and Interfaces
    3
    發行號8
    DOIs
    出版狀態Published - 24 八月 2011

    指紋

    深入研究「A novel tunable green- to yellow-emitting β-YFS:Ce <sup>3+</sup> phosphor for solid-state lighting」主題。共同形成了獨特的指紋。

    引用此