A high-temperature x-ray-diffraction study of epitaxial PbTiO3 thin films on MgO(100) grown by metal-organic chemical-vapor deposition

R. S. Batzer*, Bi Ming Yen, Donhang Liu, Haydn Chen, H. Kubo, G. R. Bai

*此作品的通信作者

研究成果: Article同行評審

25 引文 斯高帕斯(Scopus)

摘要

Epitaxial lead titanate (PbTiO3) thin films were grown on MgO(100) single-crystal substrate by metal-organic chemical-vapor deposition at a growth temperature of 650 °C. The films were dense, stoichiometric, and epitaxial. The domain structure was studied via x-ray-diffraction ω scans and in-plane Φ scans. Existence of c and a domains in the PbTiO3 films was evident. Consistent with literature reports, the a domains were found to have four variants 90° apart from each other, tilting about 2.2° away from the surface normal. The population ratio between c and a domain of the PbTiO3 films was determined to be approximately 2.3 to 1. The domain structure was found to be stable and reproducible during repeated thermal cycling above and below Tc. Furthermore, lattice parameters and Curie temperatures of PbTiO3 thin films were measured during the thermal cycles. The lattice parameters were found to be smaller and the Curie temperatures were shifted lower than the corresponding bulk values. This is attributed to the film stress effect. A theory based on the Landau-Ginzburg-Devonshire function has been developed to explain the shift of the Curie temperatures.

原文English
頁(從 - 到)6235-6242
頁數8
期刊Journal of Applied Physics
80
發行號11
DOIs
出版狀態Published - 1 十二月 1996

指紋

深入研究「A high-temperature x-ray-diffraction study of epitaxial PbTiO<sub>3</sub> thin films on MgO(100) grown by metal-organic chemical-vapor deposition」主題。共同形成了獨特的指紋。

引用此