Trap-assisted tunneling in aluminum-doped ZnO/indium oxynitride nanodot interlayer Ohmic contacts on p-GaN

Wen Cheng Ke, Fang Wei Lee, Cheng Yi Yang, Wei-Kuo Chen, Hao Ping Huang

Research output: Contribution to journalArticlepeer-review

4 Scopus citations


This study developed an Ohmic contact formation method for a ZnO:Al (AZO) transparent conductive layer on p-GaN films involving the introduction of an indium oxynitride (InON) nanodot interlayer. An antisurfactant pretreatment was used to grow InON nanodots on p-GaN films in a RF magnetron sputtering system. A low specific contact resistance of 1.12 � 10-4 Ω cm2 was achieved for a sample annealed at 500 �C for 30 s in nitrogen ambient and embedded with an InON nanodot interlayer with a nanodot density of 6.5 � 108 cm-2. By contrast, a sample annealed in oxygen ambient exhibited non-Ohmic behavior. X-ray photoemission spectroscopy results showed that the oxygen vacancy (Vo) in the InON nanodots played a crucial role in carrier transport. The fitting I-V characteristic curves indicated that the hopping mechanism with an activation energy of 31.6 meV and trap site spacing of 1.1 nm dominated the carrier transport in the AZO/InON nanodot/p-GaN sample. Because of the high density of donor-like oxygen vacancy defects at the InON nanodot/p-GaN interface, positive charges from the underlying p-GaN films were absorbed at the interface. This led to positive charge accumulation, creating a narrow depletion layer; therefore, carriers from the AZO layer passed through InON nanodots by hopping transport, and subsequently tunneling through the interface to enter the p-GaN films. Thus, AZO Ohmic contact can be formed on p-GaN films by embedding an InON nanodot interlayer to facilitate trap-assisted tunneling.

Original languageEnglish
Article number155303
JournalJournal of Applied Physics
Issue number15
StatePublished - 21 Oct 2015


Dive into the research topics of 'Trap-assisted tunneling in aluminum-doped ZnO/indium oxynitride nanodot interlayer Ohmic contacts on p-GaN'. Together they form a unique fingerprint.

Cite this